These 100-pack of 12 x 16in metal-in static shield bags feature a film printing process per MIL-PRF-81705E section 3.6 standards. This buried layer will not rub off or remove with chemicals, like IPA.
These 100-pack of 12 x 16in metal-in static shield bags feature a film printing process per MIL-PRF-81705E section 3.6 standards. This buried layer will not rub off or remove with chemicals, like IPA.
This features standard stock bags that are converted per MIL-DTL-117H.
Features
Tensile Strength | Typical Value: 4,600psi, 32mPa; Testing Method: ASTM D882 |
Puncture Resistance | Typical Value: 12lbs, 53N; Testing Method: MIL-STD-3010 Method 2065 |
Seam Strength | Typical Value: Pass; Testing Method: MIL-STD-3010 Method 2024 |
Thickness | Typical Value: 2.8mils, 0.071mm ±10%; Testing Method: MIL-STD-3010 Method 1003 |
Marking Abrasion Resistance | Typical Value: Pass; Testing Method: MIL-PRF-81705E Method 4.6.6 |
Contact Corrosivity | Typical Value: Pass; Testing Method: MIL-STD-3010 Method 3005* |
Transparency | Typical Value: 40%; Testing Method: MIL-STD-3010 Method 4034 |
EMI Attenuation | Typical Value: ≥ 10db; Testing Method: MIL-PRF-81705E Method 4.6.7 |
ESD Shielding | Typical Value: ≤ 10nJ; Testing Method: MIL-PRF-81705E Method 4.6.9 |
Surface Resistivity - Interior | Typical Value: ≥ 1 x 10&sup5; to <1 x 10¹2;Ω/sq; Testing Method: MIL-PRF-81705E Method 4.6.8 |
Surface Resistivity - Exterior | Typical Value: < 1 x 10¹2;Ω/sq; Testing Method: MIL-PRF-81705E Method 4.6.8 |
Static Decay | Typical Value: ≤ 2 seconds; Testing Method: MIL-STD-3010 Method 4046 |
Temperature/td> | 360°F (182°C) |
Time | 2 seconds |
Pressure | 60psi, 414kPa |
Tensile Strength | Typical Value: 4,600psi, 32mPa; Testing Method: ASTM D882 |
Puncture Resistance | Typical Value: 12lbs, 53N; Testing Method: MIL-STD-3010 Method 2065 |
Seam Strength | Typical Value: Pass; Testing Method: MIL-STD-3010 Method 2024 |
Thickness | Typical Value: 2.8mils, 0.071mm ±10%; Testing Method: MIL-STD-3010 Method 1003 |
Marking Abrasion Resistance | Typical Value: Pass; Testing Method: MIL-PRF-81705E Method 4.6.6 |
Contact Corrosivity | Typical Value: Pass; Testing Method: MIL-STD-3010 Method 3005* |
Transparency | Typical Value: 40%; Testing Method: MIL-STD-3010 Method 4034 |
EMI Attenuation | Typical Value: ≥ 10db; Testing Method: MIL-PRF-81705E Method 4.6.7 |
ESD Shielding | Typical Value: ≤ 10nJ; Testing Method: MIL-PRF-81705E Method 4.6.9 |
Surface Resistivity - Interior | Typical Value: ≥ 1 x 10&sup5; to <1 x 10¹2;Ω/sq; Testing Method: MIL-PRF-81705E Method 4.6.8 |
Surface Resistivity - Exterior | Typical Value: < 1 x 10¹2;Ω/sq; Testing Method: MIL-PRF-81705E Method 4.6.8 |
Static Decay | Typical Value: ≤ 2 seconds; Testing Method: MIL-STD-3010 Method 4046 |
Temperature/td> | 360°F (182°C) |
Time | 2 seconds |
Pressure | 60psi, 414kPa |